The impedance analysis of sintered MgTiO3 ceramics
(Elsevier, 2017)
In the present study the effect of preparation conditions on microstructure and electrical properties of MgTiO3 ceramics was investigated. Mixture of MgO and TiO2 powders was subjected to mechanical activation for different ...
Preparation and characterization of bismuth germanium oxide (BGO) polymer composites
(Elsevier, 2017)
Bismuth germanium oxide Bi12GeO20 (BGO) has very interesting electrical, optical and magnetic properties. In order to make devices based on this material more flexible, its powder was used for preparing polymer composites. ...
The influence of mechanical activation on structural evolution of nanocrystalline SrTiO3 powders
(Elsevier, 2017)
Structural changes caused by mechanical activation of SrTiO3 powders were investigated using a variety of methods. Average crystallite size continuously decreased with increased activation time to around 20 nm after 120 ...
The influence of mechanical activation on structural evolution of nanocrystalline SrTiO3 powders
(Elsevier, 2017)
Structural changes caused by mechanical activation of SrTiO3 powders were investigated using a variety of methods. Average crystallite size continuously decreased with increased activation time to around 20 nm after 120 ...
Insertion of lithium ion in anatase TiO2 nanotube arrays of different morphology
(Elsevier, 2017)
Anatase TiO2 nanotube arrays of different morphology were prepared by a two-step process: anodic oxidation at voltages 20–60 V and subsequent annealing at 400 °C. By amplifying anodization voltage the inner diameter of ...
Preparation and characterization of bismuth germanium oxide (BGO) polymer composites
(Elsevier, 2017)
Bismuth germanium oxide Bi12GeO20 (BGO) has very interesting electrical, optical and magnetic properties. In order to make devices based on this material more flexible, its powder was used for preparing polymer composites. ...
The impedance analysis of sintered MgTiO3 ceramics
(Elsevier, 2017)
In the present study the effect of preparation conditions on microstructure and electrical properties of MgTiO3 ceramics was investigated. Mixture of MgO and TiO2 powders was subjected to mechanical activation for different ...
Insertion of lithium ion in anatase TiO2 nanotube arrays of different morphology
(Elsevier, 2017)
Anatase TiO2 nanotube arrays of different morphology were prepared by a two-step process: anodic oxidation at voltages 20–60 V and subsequent annealing at 400 °C. By amplifying anodization voltage the inner diameter of ...