The LiFe(1-x)VxPO4/C Composite Synthesized by Gel-Combustion Method, with Improved Rate Capability and Cycle Life in Aerated Aqueous Solutions
(Elsevier, 2013)
The nitrate-(glycine + malonic acid)-assisted gel-combustion process, followed by a heat treatment at 750 °C under reductive atmosphere, was used as a fast and effective way to synthesize vanadium doped olivine incorporated ...
Electrochemical synthesis and characterization of poly(o-toluidine) as high energy storage material
(Elsevier, 2019)
Poly(o-toluidine) (POT) is electrochemically synthesized on graphite electrode at
constant current density of 1.5 mA cm-2 from aqueous electrolyte of 1.0 mol dm-3 H2SO4 and
0.25 mol dm-3 o-toluidine. Electrochemical ...
Electrochemical synthesis and characterization of poly(o-toluidine) as high energy storage material
(Elsevier, 2019)
Poly(o-toluidine) (POT) is electrochemically synthesized on graphite electrode at
constant current density of 1.5 mA cm-2 from aqueous electrolyte of 1.0 mol dm-3 H2SO4 and
0.25 mol dm-3 o-toluidine. Electrochemical ...
Pt supported on nano-tungsten carbide as a beneficial catalyst for the oxygen reduction reaction in alkaline solution
(Elsevier, 2012)
Platinum nanocatalyst at nano-tungsten carbide was synthesized, characterized and tested for oxygen reduction reaction (ORR) in 0.1 mol dm−3 NaOH, at 25 °C. Tungsten-carbide islands on nano-tungsten particles (WC) was ...
Oxygen reduction on SILAR deposited iron oxide onto graphite felt electrode
(Elsevier, 2016)
The potential characteristics of graphite felt electrodes, modified by iron oxide, for oxygen reduction are evaluated. Modification is carried out by Successive Ion Layer Adsorption and Reaction (SILAR) method, using a ...
Ti substrate coated with composite Cr–MoO2 coatings as highly selective cathode materials in hypochlorite production
(Elsevier, 2013)
The aim of this work was to investigate the possibility of preparation of the composite Cr–MoO2 coatings onto steel and titanium substrates as cathode materials with high selective properties which imply the suppression ...
Photoelectochemical behavior of TiO2-NT’s modified with SILAR deposited iron oxide
(Elsevier, 2016)
The fast reaction of forced hydrolysis of iron(III) nitrate in hypochlorite solution at room temperature, leads to the formation of mainly hematite, α-Fe2O3. Successive ion adsorption and reaction (SILAR) is applied to ...