Intergranular area microalloyed aluminium-silicate ceramics fractal analysis
(Belgrade : International Institute for the Science of Sintering, 2013)
Porous aluminium-silicate ceramics, modified by alloying with magnesium and microalloying with alluminium belongs to a group of advanced multifunctional ceramics materials. This multiphase solid-solid system has predominantly ...
ZnTiO3 ceramic nanopowder microstructure changes during compaction
(Belgrade : International Institute for the Science of Sintering, 2013)
ZnTiO3 nanopowder as a constitutive component in compact production was primarily characterized. Scanning electron micrographs of as received powder were recorded. Mercury porosimetry and nitrogen adsorption were also ...
The influence of mechanochemical activation and thermal treatment on magnetic properties of the BaTiO3 -FexOy powder mixture
(Belgrade : International Institute for the Science of Sintering, 2015)
Powder mixture of 50 mass % of barium titanate (BaTiO3) and 50 mass % of iron (Fe) was prepared by solid-state reaction technique, i.e. ball milled in air for 60 min, 80 min, 100 min, 120 min and 150 min. During mechanochemical ...
The fractal nature materials microstructure influence on electrochemical energy sources
(Belgrade : International Institute for the Science of Sintering, 2015)
With increasing of the world energy crisis, research for new, renewable and alternative energy sources are in growth. The focus is on research areas, sometimes of minor importance and applications, where the different ...
Influence of nitrogen and air atmosphere during thermal treatment on micro and nano sized powders and sintered TiO2 specimens
(Belgrade : International Institute for the Science of Sintering, 2014)
The influence of air and nitrogen atmosphere during heating on TiO2 nano and micro sized powders as well as sintered polycrystalline specimens was analyzed. Sintering of TiO2 nano and micro powders in air atmosphere was ...
The influence of mechanical activation on sintering process of BaCO3-SrCO3-TiO2 system
(Belgrade : International Institute for the Science of Sintering, 2012)
In this article the influence of mechanical activation on sintering process of bariumstrontium-titanate ceramics has been investigated. Both non-activated and mixtures treated in a planetary ball mill for 5, 10, 20, 40, ...
Mechanical activation as sintering pre-treatment of talc for steatite ceramics
(Belgrade : Interenational Institute for the Science of Sintering, 2014)
The effect of vibratory mill induced mechanical activation on the change of the particle size, crystallinity and the phase transformations of the minerals present in the activated material, was studied with the purpose of ...
Characterisation of Mn0.63Zn0.37Fe2O4 powders after intensive milling and subsequent thermal treatment
(Science of Sintering, 2017)
Commercial Mn-Zn powder (Mn0.63Zn0.37Fe2O4, 93 wt. % and Fe2O3 7 wt. %) was milled 0.5, 1, 2 and 4 hours in a planetary ball mill. The goal was to observe intensive milling influences on oxidation and reduction processes ...
Physical Properties of Sintered Alumina Doped with Different Oxides
(Belgrade : ETRAN, 2018)
Corundum (α-alumina) is a suitable material for usage in various industry fields owing to its chemical stability, electrical and mechanical features. It is known that properties of ceramics could be modified by addition ...
Structure and photocatalytic properties of sintered TiO2 nanotube arrays
(Belgrade : ETRAN, 2018)
One-dimensional (1D) TiO2 nanotubes perpendicular to the substrate were obtained by electrochemical oxidation of titanium foil in an acid electrolyte. In order to alter the crystallinity and the morphology of films the ...