Electrical properties of mechanochemicaly activated cordierite ceramics
(Kiev, 2009)
Three-component oxide mixture was prepared containing MgO+Al2O3+SiO2 in a 2:2:5 ratio with addition of 10% Bi203. Mixtures were mechanically activated in range from 5 to 240 minutes in a mill with ceramic balls, and sintered ...
Electrical properties of mechanochemically activated cordierite ceramics
(Springer, 2012)
Three-component oxide mixtures were prepared containing MgO, Al 2 O 3 and SiO 2 in a 2 : 2 : 5 ratio with addition of 10% Bi 2 O 3. The mixtures were mechanically activated in a range from 5 to 240 min in a mill with ceramic ...
Compaction pressure's influence on density and electrical properties of sintered cordierite-based ceramics
(Belgrade : Materials Research Society of Serbia; Institute of Technical Sciences of SASA; Vinča Institute of Nuclear Sciences, University of Belgrade, 2012)
Mechanical activation is widely used for sample preparation before the sintering process. However, the influence of pressure, which is used for compaction, has not been completely investigated. Cordierite, 2MgO_2Al2O3_5SiO2, ...
Influence of MoO3 on sintering temperature of mechanically activated MgO-Al2O3-SiO2 system
(Belgrade : Serbian Ceramic Society, 2013)
Cordierite, 2MgO⋅2Al2O3⋅5SiO2, is a very attractive high-temperature ceramic material, due to its outstanding electrical characteristics, such as the low temperature expansion coefficient, low dielectric constant and good ...
Density and electrical properties of cordierite based ceramics as function of compaction pressure
(Belgrade : Serbian Ceramic Society, 2013)
Mechanical activation is widely used and relatively inexpensive procedure for sintering process sample preparation. However, the influence of pressure, which is used for compaction, has not been completely investigated. ...
Influence of Mechanical Activation on the Constituents of the MgO-Al2O3-SiO2-TiO2 System
(Belgrade : Serbian Ceramic Society, 2012)
Cordierite, 2MgO2Al2O35SiO2, is a very attractive high-temperature ceramic material, due to its outstanding electrical characteristics, such as the low temperature expansion coefficient, low dielectric constant and good ...
The Electrical Characteristics of Nb doped BaTiO3 Ceramics
(Belgrade : Serbian Ceramic Society, 2014)
The Nb doped BaTiO3 ceramics, with different Nb2O5 content, ranging from 0.5 to 2.0 at% Nb, were investigated regarding their electrical characteristics in this paper. Nb/BaTiO3 ceramics using in this investigation were ...
Influence of one activated component on the sintering process of three phase system
(Belgrade : Materials Research Society of Serbia, 2013)
According to its low temperature thermal expansion coefficient, low dielectric constant, also good mechanical properties, cordierite, 2MgO×2Al2O3×5SiO2, represents a very attractive hightemperature ceramic material. In ...
Influence of MoO3 on cordierite ceramics sintering and crystallization
(Belgrade : Materials Research Society of Serbia, 2013)
The influence of MoO3 on the process of cordierite ceramics preparation, 2MgO-2Al2O3-5SiO2 (MAS) was researched by sintering followed binary systems: MgO/MoO3 (sintered at 850 ºC and 1000 ºC), Al2O3/Bi2O3 and SiO2/Bi2O3 ...
Uticaj mehaničke energije na komponente MgO-Al2O3-SiO2-TiO2 sistema
(Beograd : Savez inženjera i tehničara Srbije, 2012)
U ovom radu je ispitivan uticaj mehaničke energije na strukturu i promene u mikrostrukturi sistema MgO-Al2O3-SiO2-TiO2. Utvrđeno je da mehanička energija pospešuje homogenizaciju polaznih komponenti, utiče na veličinu i ...