Structural and electrical properties of barium-zinc-titanate ceramics sintered at 1300ºc
Pavlović, Vladimir B.
Ristić, Momčilo M.
Остала ауторстваUskoković, Dragan
МетаподациПриказ свих података о документу
The aim of this work was an investigation of structural and electrical properties of sintered barium-zinc-titanate ceramics. Mixtures of BaCO3, ZnO and TiO2 were mechanically activated in a planetary ball mill up to 80 minutes and sintered isothermally in air for 120 minutes at 1300°C. The phase composition in the BaCO3-ZnO-TiO2 system after milling and sintering was analyzed using the XRD method. The existence of pure barium-zinc-titanate has been registered. Microstructure analyses were performed using SEM. The results of electric resistivity, capacitance and loss tangent of the sintered samples were correlated with the XRD and SEM results.
Кључне речи:barium zinc titanate ceramics / sintering / electrical properties
Извор:Programme and The Book of Abstracts / Twelfth Annual Conference YUCOMAT 2010, Herceg Novi, September 6–10, 2010, 2010, 118-118
- Belgrade : Institute of Technical Sciences of SASA
ISBN: 9788680321189[ Google Scholar ]