Electrical and transport properties of nickel manganite obtained by Hall effect measurements
Samo za registrovane korisnike
AutoriSavić, Slavica M.
Stojanović, G. M.
Nikolić, Maria Vesna
Aleksić, Obrad S.
Luković Golić, Danijela
Nikolić, Pantelija M.
Članak u časopisu (Objavljena verzija)
MetapodaciPrikaz svih podataka o dokumentu
Intrinsic resistivity and carrier transport parameters of sintered nickel manganite samples (NTC thermistor grade) were determined using a Hall effect measurement system based on the van der Pauw method. Powder mixtures composed of MnO, NiO and with small amounts of CoO and Fe 2O 3 were free surface energy activated by milling in an ultra fast planetary mill for 5, 15, 30, 45 and 60 min. The powders were uniaxially pressed with 196 MPa into discs and sintered at 1200 °C for 60 min. Full characterization of nickel manganite samples was done using SEM, EDS and XRD analysis. The Hall effect was measured at different temperatures (room temperature, 50, 80, 100 and 120 °C) with an applied field of 0.37 T and also 0.57 T at room temperature. The activation energy E a (energy of conduction) and the coefficient of temperature sensitivity B 25/80, were calculated from measured resistivity values. The measured mobility, resistivity/conductivity, U-I plots, and Hall coefficients were mutually com...pared and correlated versus microstructure development and macroscopic parameters such as the powder activation time and ambient temperature. © Springer Science+Business Media, LLC 2008.
Ključne reči:nickel manganite / Hall effect / electrical properties / transport properties
Izvor:Journal of Materials Science: Materials in Electronics, 2009, 20, 3, 242-247