dc.description.abstractStarting mixtures of ZnO, TiO2 and MgO (0, 1.25 and 2.5 wt.% MgO) powders were mechanically activated for 15 min in a planetary ball mill. The powders obtained were sintered non-isothermally to temperatures between 800 and 1100 °C and then held at those temperatures for 120 min. Analysis of the influence of MgO addition on the synthesis of zinc-titanate ceramics showed that its addition increased slightly the temperature at which the reaction process started, accelerated the reaction and resulted in higher sample densities. These results were correlated with the results of structural characterization using X-ray powder diffraction method and SEM analysis. Also, the results of electric resistivity, capacitance and loss tangent of the sintered samples were obtained. © 2008 Elsevier B.V. All rights reserved.
dc.publisherElsevier
dc.relationinfo:eu-repo/grantAgreement/MESTD/MPN2006-2010/142011/RS//
dc.rightsrestrictedAccess
dc.sourceJournal of Alloys and Compounds
dc.subjectsintering
dc.subjectceramics
dc.subjectmechanochemical processing
dc.subjectX-ray diffraction
dc.titleInfluence of MgO addition on the synthesis and electrical properties of sintered zinc-titanate ceramics
dc.typearticleen
dc.rights.licenseARR
dcterms.abstractОбрадовић, Нина; Митрић, Миодраг; Николић, Мариа Весна; Ристић, Момчило М.; Минић, Драгица; Митровић, Небојша;
dc.citation.spage272
dc.citation.epage277
dc.citation.volume471
dc.citation.issue1-2
dc.identifier.doi10.1016/j.jallcom.2008.03.090
dc.identifier.scopus2-s2.0-60949090871
dc.type.versionpublishedVersion
dc.identifier.fulltexthttp://dais.sanu.ac.rs/bitstream/handle/123456789/3465/Obradovic_Journal-of-Alloys-and-Compounds_471_2009_272_277.pdf


Документи

Thumbnail

Овај рад се појављује у следећим колекцијама

Приказ основних података о документу