Structural and dielectric properties of BaTi1-xSnxO3 ceramics
Само за регистроване кориснике
Конференцијски прилог (Објављена верзија)
МетаподациПриказ свих података о документу
BaTi1-xSnO3 (BTS) powders, with x ranging from 0 to 1, were synthesized by solid-state reaction technique. The powders were pressed into pellets and sintered at 1370 and 1420 T. The structural characterization of sintered BTS samples was made at room temperature using X-ray diffraction and Raman spectroscopy measurements. The BTS samples were found to be single-phase solid solutions. Dielectric properties of sintered BTS samples were studied as a function of sintering temperatures and tin contents, too. For samples with x ranging from 0 up to 0.15, it has been found that the Curie temperature decreases while the maximum of the dielectric constant increases with increasing tin content. These samples have relatively high dielectric constants, contrary to x GT 0.2 samples with very low dielectric constants. It is noticed that BTS ceramics sintered at 1420 degrees C exhibit better dielectric properties than those sintered at 1370 degrees C.
Кључне речи:BaTi1-xSnxO3 / dielectric properties / phase transformation / solid state reaction / XRD
Извор:Recent Developments in Advanced Materials and Processes, 7th Conference of the Yugoslav-Materials-Research-Society (Yu-MRS), Sep 12-16, 2005, Herceg Novi, Montenegro, 2006, 241-246
- Синтеза функционалних материјала са контролисаном структуром на молекуларном и нано нивоу (RS-142006)