Properties of the cement-based composites with high content of metakaolin
Само за регистроване кориснике
Конференцијски прилог (Објављена верзија)
МетаподациПриказ свих података о документу
Environmental concerns and sustainable development require increased replacement of cement. Most of previous studies have shown that the compressive strength of cement-based composites is maximized with a 20% content of metakaolin. We investigated composites prepared by replacing ordinary Portland Cement (OPC) with 30 to 50% of metakaolin (MK) and addition of appropriate amount of hydrated lime, which were ordinary cured for 2, 28 or 90 days. Hydration products and microstructure of the pastes were determined by X-ray diffraction (XRD), differential thermal analysis/thermal gravimetry (DTA/TG) and mercury intrusion porosimetry (MIP). MK was produced by calcination of kaolin from a Serbian deposit, which contained a high level of impurities. Replacement of OPC with 30% of MK achieved 28 days compressive strength equivalent to that of the control mix. Higher replacement levels, 40% and 50%, combined with the addition of hydrated lime, achieved satisfactory relative strengths of 94% an...d 87%, respectively. The positive contribution was particularly pronounced after 90 days for a composite containing 50% of MK. The results clearly showed a possibility of obtaining composites having acceptable compressive strength with reduced cement content in accordance with environmental and sustained development requirements.
Кључне речи:metakaolin / hydrated lime / cement-based composites / compressive strength
Извор:Calcined Clays for Sustainable Concrete: Proceedings of the 2nd International Conference on Calcined Clays for Sustainable Concrete, 2018
- Dordrecht : Springer