TEM analysis with EDS of β NaY0.78F4:Yb0.2Tm0.02; System 1 EDTA, Experiment 1, Samples Hex@TiO2Acac & Hex@TiO2Acac 300
Апстракт
TEM analysiswith EDS of α NaY0.78F4:Yb0.2Tm0.02, were analyzed on JEM 2100F operating at 200kV. Samples were synthesized for CORE-SHELL Project through EDTA assisted solvothermal processing, Et:H2O=2:1, FF=60 %, c=0.01 M, 200oC/2h; Re:NaF=1:7, Re:EDTA=1:1, and coated withTiO2-Acac. Data were collected on 11/23/2022.
***Dataset contents:***
EDS-Sample-Hex -TiO2acac-300a.tif (576.9Kb)
EDS-Sample-Hex1-TiO2acac-300b.tif (448.9Kb)
EDS-Sample-Hex1-TiO2acac-300c.tif (107.0Kb)
SAED-Sample-Hex1-TiO2acac.tif (439.9Kb)
TEM-Sample-Hex1-TiO2acac-300a.tif (14.02Mb)
TEM-Sample-Hex1-TiO2acac-300b.tif (14.67Mb)
TEM-Sample-Hex1-TiO2acac-300c.tif (16.14Mb)
TEM-Sample-Hex1-TiO2acac-300d.tif (15.98Mb)
TEM-Sample-Hex1-TiO2acac-300e.tif (14.90Mb)
TEM-Sample-Hex1-TiO2acac-300f.tif (14.75Mb)
TEM-Sample-Hex1-TiO2acac-a.tif (14.76Mb)
TEM-Sample-Hex1-TiO2acac-b.tif (14.70Mb)
TEM-Sample-Hex1-TiO2acac-c.tif (17.14Mb)
TEM-Sample_Hex1_TiO2acac_300g.tif (17.39Mb)
README-TEM-Hex.txt
Кључне речи:
NaYF4;Yb,Tm@TiO2-acac hexagonal / EDTA assisted solvothermal process / Transmission electron microscopy (TEM) / Energy-dispersive X-ray spectroscopy (EDS)Извор:
2022Издавач:
- Rio de Janeiro : Federal University of Rio de Janeiro, Department of Metallurgical and Materials Engineering
Финансирање / пројекти:
- CORE-SHELL Project
Напомена:
- EDS analysis confirmed the presence of all constituent elements in the sample Hex1 TiO2acac 300.
- Data were published in the paper: https://doi.org/10.3390/ijms24119441
Повезане информације:
- Повезани садржај
https://doi.org/10.3390/ijms24119441
Колекције
Институција/група
Институт техничких наука САНУ / Institute of Technical Sciences of SASATY - DATA PY - 2022 UR - https://dais.sanu.ac.rs/123456789/14271 AB - TEM analysiswith EDS of α NaY0.78F4:Yb0.2Tm0.02, were analyzed on JEM 2100F operating at 200kV. Samples were synthesized for CORE-SHELL Project through EDTA assisted solvothermal processing, Et:H2O=2:1, FF=60 %, c=0.01 M, 200oC/2h; Re:NaF=1:7, Re:EDTA=1:1, and coated withTiO2-Acac. Data were collected on 11/23/2022. AB - ***Dataset contents:*** EDS-Sample-Hex -TiO2acac-300a.tif (576.9Kb) EDS-Sample-Hex1-TiO2acac-300b.tif (448.9Kb) EDS-Sample-Hex1-TiO2acac-300c.tif (107.0Kb) SAED-Sample-Hex1-TiO2acac.tif (439.9Kb) TEM-Sample-Hex1-TiO2acac-300a.tif (14.02Mb) TEM-Sample-Hex1-TiO2acac-300b.tif (14.67Mb) TEM-Sample-Hex1-TiO2acac-300c.tif (16.14Mb) TEM-Sample-Hex1-TiO2acac-300d.tif (15.98Mb) TEM-Sample-Hex1-TiO2acac-300e.tif (14.90Mb) TEM-Sample-Hex1-TiO2acac-300f.tif (14.75Mb) TEM-Sample-Hex1-TiO2acac-a.tif (14.76Mb) TEM-Sample-Hex1-TiO2acac-b.tif (14.70Mb) TEM-Sample-Hex1-TiO2acac-c.tif (17.14Mb) TEM-Sample_Hex1_TiO2acac_300g.tif (17.39Mb) README-TEM-Hex.txt PB - Rio de Janeiro : Federal University of Rio de Janeiro, Department of Metallurgical and Materials Engineering T1 - TEM analysis with EDS of β NaY0.78F4:Yb0.2Tm0.02; System 1 EDTA, Experiment 1, Samples Hex@TiO2Acac & Hex@TiO2Acac 300 UR - https://hdl.handle.net/21.15107/rcub_dais_14271 ER -
@misc{ year = "2022", abstract = "TEM analysiswith EDS of α NaY0.78F4:Yb0.2Tm0.02, were analyzed on JEM 2100F operating at 200kV. Samples were synthesized for CORE-SHELL Project through EDTA assisted solvothermal processing, Et:H2O=2:1, FF=60 %, c=0.01 M, 200oC/2h; Re:NaF=1:7, Re:EDTA=1:1, and coated withTiO2-Acac. Data were collected on 11/23/2022., ***Dataset contents:*** EDS-Sample-Hex -TiO2acac-300a.tif (576.9Kb) EDS-Sample-Hex1-TiO2acac-300b.tif (448.9Kb) EDS-Sample-Hex1-TiO2acac-300c.tif (107.0Kb) SAED-Sample-Hex1-TiO2acac.tif (439.9Kb) TEM-Sample-Hex1-TiO2acac-300a.tif (14.02Mb) TEM-Sample-Hex1-TiO2acac-300b.tif (14.67Mb) TEM-Sample-Hex1-TiO2acac-300c.tif (16.14Mb) TEM-Sample-Hex1-TiO2acac-300d.tif (15.98Mb) TEM-Sample-Hex1-TiO2acac-300e.tif (14.90Mb) TEM-Sample-Hex1-TiO2acac-300f.tif (14.75Mb) TEM-Sample-Hex1-TiO2acac-a.tif (14.76Mb) TEM-Sample-Hex1-TiO2acac-b.tif (14.70Mb) TEM-Sample-Hex1-TiO2acac-c.tif (17.14Mb) TEM-Sample_Hex1_TiO2acac_300g.tif (17.39Mb) README-TEM-Hex.txt", publisher = "Rio de Janeiro : Federal University of Rio de Janeiro, Department of Metallurgical and Materials Engineering", title = "TEM analysis with EDS of β NaY0.78F4:Yb0.2Tm0.02; System 1 EDTA, Experiment 1, Samples Hex@TiO2Acac & Hex@TiO2Acac 300", url = "https://hdl.handle.net/21.15107/rcub_dais_14271" }
(2022). TEM analysis with EDS of β NaY0.78F4:Yb0.2Tm0.02; System 1 EDTA, Experiment 1, Samples Hex@TiO2Acac & Hex@TiO2Acac 300. Rio de Janeiro : Federal University of Rio de Janeiro, Department of Metallurgical and Materials Engineering.. https://hdl.handle.net/21.15107/rcub_dais_14271
TEM analysis with EDS of β NaY0.78F4:Yb0.2Tm0.02; System 1 EDTA, Experiment 1, Samples Hex@TiO2Acac & Hex@TiO2Acac 300. 2022;. https://hdl.handle.net/21.15107/rcub_dais_14271 .
"TEM analysis with EDS of β NaY0.78F4:Yb0.2Tm0.02; System 1 EDTA, Experiment 1, Samples Hex@TiO2Acac & Hex@TiO2Acac 300" (2022), https://hdl.handle.net/21.15107/rcub_dais_14271 .