Characterization of MgAl2O4 sintered ceramics

Obradović, Nina; Fahrenholtz, William G.; Filipović, Suzana; Corlett, Cole; Đorđević, Pavle; Rogan, Jelena; Vulić, Predrag J.; Buljak, Vladimir; Pavlović, Vladimir B.

(ETRAN, 2019)

TY  - JOUR
AU  - Obradović, Nina
AU  - Fahrenholtz, William G.
AU  - Filipović, Suzana
AU  - Corlett, Cole
AU  - Đorđević, Pavle
AU  - Rogan, Jelena
AU  - Vulić, Predrag J.
AU  - Buljak, Vladimir
AU  - Pavlović, Vladimir B.
PY  - 2019
UR  - http://dais.sanu.ac.rs/123456789/6949
AB  - Single phase MgAl2O4 was made from a one-to-one molar ratio of MgO and Al2O3 powders mixed using ball-milling. Mixtures of MgO and Al2O3 were subsequently treated in planetary ball mill for 30, 60, 90 and 120 minutes in air. The aim of this study was to examine phase composition, microstructure, and densification behavior of sintered specimens. After sintering in dilatometer at 1500 °C, the powder was converted to single phase MgAl2O4. The results show that mechanical activation improved the densification behavior of MgAl2O4 sintered specimens, and it reduced the onset temperature for sintering by approx. 100 oC. Based on dilatometer data, powders were subsequently densified at 1450 oC by hot pressing. Almost аll specimens exhibited full density, while sample activated for 30 minutes showed the fastest densification rate.
PB  - ETRAN
T2  - Science of Sintering
T1  - Characterization of MgAl2O4 sintered ceramics
SP  - 363
EP  - 376
VL  - 51
IS  - 4
DO  - 10.2298/SOS1904363O
ER  - 
@article{
author = "Obradović, Nina and Fahrenholtz, William G. and Filipović, Suzana and Corlett, Cole and Đorđević, Pavle and Rogan, Jelena and Vulić, Predrag J. and Buljak, Vladimir and Pavlović, Vladimir B.",
year = "2019",
url = "http://dais.sanu.ac.rs/123456789/6949",
abstract = "Single phase MgAl2O4 was made from a one-to-one molar ratio of MgO and Al2O3 powders mixed using ball-milling. Mixtures of MgO and Al2O3 were subsequently treated in planetary ball mill for 30, 60, 90 and 120 minutes in air. The aim of this study was to examine phase composition, microstructure, and densification behavior of sintered specimens. After sintering in dilatometer at 1500 °C, the powder was converted to single phase MgAl2O4. The results show that mechanical activation improved the densification behavior of MgAl2O4 sintered specimens, and it reduced the onset temperature for sintering by approx. 100 oC. Based on dilatometer data, powders were subsequently densified at 1450 oC by hot pressing. Almost аll specimens exhibited full density, while sample activated for 30 minutes showed the fastest densification rate.",
publisher = "ETRAN",
journal = "Science of Sintering",
title = "Characterization of MgAl2O4 sintered ceramics",
pages = "363-376",
volume = "51",
number = "4",
doi = "10.2298/SOS1904363O"
}
Obradović, N., Fahrenholtz, W. G., Filipović, S., Corlett, C., Đorđević, P., Rogan, J., Vulić, P. J., Buljak, V.,& Pavlović, V. B. (2019). Characterization of MgAl2O4 sintered ceramics.
Science of SinteringETRAN., 51(4), 363-376.
https://doi.org/10.2298/SOS1904363O
Obradović N, Fahrenholtz WG, Filipović S, Corlett C, Đorđević P, Rogan J, Vulić PJ, Buljak V, Pavlović VB. Characterization of MgAl2O4 sintered ceramics. Science of Sintering. 2019;51(4):363-376
Obradović Nina, Fahrenholtz William G., Filipović Suzana, Corlett Cole, Đorđević Pavle, Rogan Jelena, Vulić Predrag J., Buljak Vladimir, Pavlović Vladimir B., "Characterization of MgAl2O4 sintered ceramics" 51, no. 4 (2019):363-376,
https://doi.org/10.2298/SOS1904363O .
2
2